特點：
1、綜合性能較好，沖擊強度較高，化學穩定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現白化現象。
| Polykemi AB POLYblend 6005B PC/ABS-Blend | |||
|---|---|---|---|
| Categories: | Polymer; Thermoplastic; ABS Polymer; Polycarbonate/ABS Alloy, Unreinforced; Polycarbonate (PC)
|
||
| Material Notes: |
Information provided by Polykemi AB |
||
| Key Words: | PC/ABS | ||
| Vendors: | No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material. | ||
|
|||
Printer friendly version 
Download as PDF
Download to Excel (requires Excel and Windows)
Export data to your CAD/FEA program| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | With Flow; ISO 2577 |
| 0.0080 - 0.010 cm/cm | 0.0080 - 0.010 in/in | Across Flow; ISO 2577 | |
| Melt Index of Compound | 14 g/10 min @Load 5.00 kg, Temperature 240 °C |
14 g/10 min @Load 11.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 @Time 15.0 sec |
62 @Time 0.00417 hour |
ASTM D2240 |
| Tensile Strength at Break | <= 45.0 MPa | <= 6530 psi | ISO/R527 |
| Elongation at Break | >= 80 % | >= 80 % | ISO/R527 |
| Flexural Strength | <= 60.0 MPa | <= 8700 psi | ISO 178 |
| Flexural Modulus | 1.80 GPa @Temperature 23.0 °C |
261 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 110 °C @Load 5.001 kg |
230 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 190 °C @Load 1.00 kg |
374 °F @Load 2.21 lb |
50°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
典型應用范圍:
汽車內外飾：儀表板，飾柱，儀表前蓋，格柵，內外飾件 2.商務設備機殼和內置部件：筆記本/臺式電腦，復印機，打印機，繪圖儀，顯示器 3.電信，移動電話外殼，附件以及智能卡（SIM卡）： 4.電器產品，電子產品外殼，電表罩和殼體，家用開關，插頭和插座，電纜電線管道 5.家用電器，如洗衣機，吹風機，微波爐內外部件等。