1、綜合性能較好，沖擊強度較高，化學穩定性，電性能良好.
2、與372有機玻璃的熔接性良好，制成雙色塑件，且可表面鍍鉻，噴漆處理.
3、有高抗沖、高耐熱、阻燃、增強、透明等級別。
4、流動性比HIPS差一點，比PMMA、PC等好，柔韌性好。
5、用途：適于制作一般機械零件，減磨耐磨零件，傳動零件和電訊零件.
6、同PVC（聚氯乙烯）一樣在屈折處會出現白化現象。
圖
| 物性表： | |||
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| High Load Melt Index | 7.0 g/10 min @Load 21.6 kg, Temperature 260 °C |
7.0 g/10 min @Load 47.6 lb, Temperature 500 °F |
|
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 116 | 116 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ATSM D638 |
| Elongation at Break | 105 % | 105 % | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 2.60 GPa | 377 ksi | ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm | 11.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | ASTM D648 |