生產型號： PC-10R-(V6) 6 MFI
生產 類別： 熱塑性聚合物；；聚碳酸酯（PC）聚碳酸酯，無筋，阻燃劑；
Tristar® PC-10R-(V6) 6 MFI原材料外包裝圖：
Tristar® PC-10R-(V6) 6 MFI原材料內顆粒圖：
Tristar® PC-10R-(V6) 6 MFI原材料概述：
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | 24 hours at 73°C; ASTM D570 | ||
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | ASTM D785 | ||
| Tensile Strength, Yield | 62.1 MPa @Thickness 3.17 mm |
9010 psi @Thickness 0.125 in |
ASTM D638 | ||
| Elongation at Break | 120 % @Thickness 3.17 mm |
120 % @Thickness 0.125 in |
ASTM D638 | ||
| Flexural Yield Strength | 89.6 MPa @Thickness 3.17 mm |
13000 psi @Thickness 0.125 in |
ASTM D790 | ||
| Flexural Modulus | 2.14 GPa @Thickness 3.17 mm |
310 ksi @Thickness 0.125 in |
ASTM D790 | ||
| Izod Impact, Notched | 8.01 J/cm @Thickness 3.17 mm |
15.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | PLC 6 | ||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC 2 | ||
| Hot Wire Ignition, HWI | 15 - 30 sec @Thickness 1.50 mm |
15 - 30 sec @Thickness 0.0591 in |
PLC 3 | ||
| 30 - 60 sec @Thickness 3.00 mm |
30 - 60 sec @Thickness 0.118 in |
PLC 2 | |||
| High Amp Arc Ignition, HAI | 60 - 120 arcs @Thickness 3.00 mm |
60 - 120 arcs @Thickness 0.118 in |
PLC 1 | ||
| >= 120 arcs @Thickness 1.50 mm |
>= 120 arcs @Thickness 0.0591 in |
PLC 0 | |||
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC 3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 70.2 µm/m-°C @Temperature -40.0 - 95.0 °C |
39.0 µin/in-°F @Temperature -40.0 - 203 °F |
Flow; ASTM E831-06 | ||
| CTE, linear, Transverse to Flow | 68.4 µm/m-°C @Temperature -40.0 - 95.0 °C |
38.0 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E831-06 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | ASTM D648 | ||
| 137 °C | 279 °F | ISO 75 | |||
| UL RTI, Electrical | 125 °C | 257 °F | |||
| UL RTI, Mechanical with Impact | 115 °C | 239 °F | |||
| UL RTI, Mechanical without Impact | 125 °C | 257 °F | |||
| Flammability, UL94 | V-2 @Thickness 1.50 mm |
V-2 @Thickness 0.0591 in |
|||
| Glow Wire Test | 775 °C | 1430 °F | GWIT | ||
| 960 °C | 1760 °F | GWFI | |||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 288 - 304 °C | 550 - 580 °F | |||
| Middle Barrel Temperature | 299 - 321 °C | 570 - 610 °F | |||
| Front Barrel Temperature | 316 - 338 °C | 600 - 640 °F | |||
| Nozzle Temperature | 304 - 332 °C | 580 - 630 °F | |||
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |||
| Mold Temperature | 82.2 - 116 °C | 180 - 240 °F | |||
| Drying Temperature | 121 °C | 250 °F | |||
| Dry Time | 3 - 4 hour | 3 - 4 hour | 48 hours max. | ||
| Injection Pressure | 110 - 152 MPa | 16000 - 22000 psi | |||
| Back Pressure | 0.345 - 1.38 MPa | 50.0 - 200 psi | |||
| Clamp Pressure | 27.6 - 68.9 MPa | 4000 - 10000 psi | |||
| Shot Size | 40 - 60 % | 40 - 60 % | |||
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | |||
| De |
|||||
| Injection Speed- Edge Gate | Slow to Medium | ||||
| Injection Speed- Tab Gate | Medium to Fast | ||||
| Injection Speed- Tunnel Gate | Fast | ||||
本公司還提供德國杜邦、美國首諾、美國PLA、日本UMG、基礎創新塑料（美國）、美國舒爾曼、美國英威達、美國RTP、美國巴斯夫、上海巴斯夫、德國巴斯夫、馬來西亞巴斯夫、 日本東麗、 日本三菱工程、 德國朗盛、德國弗瑞圣塔、荷蘭DSM、 美國DSM、 泰國杜邦、河南神馬尼龍、三井TPX、意大利泰克尼卡、意大利蘭蒂奇、意大利LATI、美國普立萬、上海羅地亞、法國羅地亞、日本尤尼卡、深圳東麗、日本旭化成、日本東洋紡織、臺灣南亞、惠州南亞、臺灣新光、 美國液氮、 臺灣太松、日本EMS、瑞士EMS、美國泰科納、加拿大英威達、加拿大杜邦、新加坡杜邦、新加坡美樂、日本杜邦、等各種工程塑料.........
PTS Tristar PC-10R 10 MFI Polycarbonate With Release
PTS Tristar PC-10R-(14) 14 MFI Polycarbonate With Release PTS Tristar PC-10R-(18) 18 MFI Polycarbonate With Release
PTS Tristar PC-10R-(22) 22 MFI Polycarbonate With Release PTS Tristar PC-10R-(6) 6 MFI Polycarbonate With Release
PTS Tristar PC-10R-(8) 8 MFI Polycarbonate With Release
PTS Tristar PC-10R-(IM) 10 MFI Impact Modified Polycarbonate With Release
PTS Tristar PC-10R-(V) 10 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(V15) 15 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(V18) 18 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(V20) 20 MFI UV Stabilized Polycarbonate with Release
PTS Tristar PC-10R-(V22) 22 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(V6) 6 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(V8) 8 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-(VE) 12 MFI UV Stabilized Polycarbonate With Release
PTS Tristar PC-10R-CL 10 MFI Clear Polycarbonate with Release
PTS Tristar PC-10R-CL(15) 15 MFI Clear Polycarbonate with Release
PTS Tristar PC-10R-CL(22) 22 MFI Clear Polycarbonate with Release
PTS Tristar PC-10R-CL(6) 6 MFI Clear Polycarbonate with Release
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產品都是原廠家，原包裝一線獨家營銷！可提供以下報告：COA（產地證明）SGS（檢測報告） MSDS（成分報告） FDA（食品安全報告） UL黃卡(出口報告)正規17%的正規發票！歡迎新老客戶來電咨詢：
聯系人：鄧小姐
聯系電話：13917657923
固定電話：021-51131842
聯系QQ：996152797
聯系信箱：996152797@qq.com