- 密度 [g/cm3]: 1.067
- 吸水率 [%]: 1.4
- 缺口沖擊強(qiáng)度: 0.59
- 彎曲強(qiáng)度 [MPa]: 140.0
- 彎曲模量 [MPa]: 4.77
- 硬度: 121.0
- 熱變形溫度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.067 g/cc | 0.03855 lb/in3 | Melt; ISO 1183 | ||
| 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 | |||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | 0.2 in/min; ASTM Test | ||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ISO Data | |||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ASTM Test | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ASTM Test | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ISO Data | |||
| 160 MPa @Temperature -40.0 °C | 23200 psi @Temperature -40.0 °F | ISO Data | |||
| 160 MPa @Temperature -40.0 °C | 23200 psi @Temperature -40.0 °F | ASTM Test | |||
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 4.0 % | 4.0 % | 5mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 0.2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ISO Data | |||
| 7.0 % @Temperature 120 °C | 7.0 % @Temperature 248 °F | ASTM Test | |||
| 8.0 % @Temperature 80.0 °C | 8.0 % @Temperature 176 °F | ASTM Test | |||
| 8.0 % @Temperature 80.0 °C | 8.0 % @Temperature 176 °F | ISO Data | |||
| Tensile Modulus | 5.96 GPa | 864 ksi | 1mm/min; ISO 527 | ||
| 2.09 GPa @Temperature 120 °C | 303 ksi @Temperature 248 °F | ISO Data | |||
| 2.47 GPa @Temperature 80.0 °C | 358 ksi @Temperature 176 °F | ISO Data | |||
| 5.95 GPa @Temperature -40.0 °C | 863 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 160 MPa | 23200 psi | ISO Data | ||
| 172 MPa | 24900 psi | ASTM Test | |||
| 76.0 MPa @Temperature 120 °C | 11000 psi @Temperature 248 °F | ASTM Test | |||
| 90.0 MPa @Temperature 93.0 °C | 13100 psi @Temperature 199 °F | ASTM Test | |||
| 110 MPa @Temperature 65.0 °C | 16000 psi @Temperature 149 °F | ASTM Test | |||
| 214 MPa @Temperature -40.0 °C | 31000 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 4.77 GPa | 692 ksi | ISO Data | ||
| 5.31 GPa | 770 ksi | ASTM Test | |||
| 1.93 GPa @Temperature 120 °C | 280 ksi @Temperature 248 °F | ASTM Test | |||
| 2.40 GPa @Temperature 65.0 °C | 348 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.590 J/cm @Thickness 3.17 mm | 1.11 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO Test | ||
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.650 J/cm2 | 3.09 ft-lb/in2 | ISO 179 | ||
| 0.550 J/cm2 @Temperature -30.0 °C | 2.62 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1.00e+6 Hz | 3.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 4.0 @Frequency 1e+9 Hz | 4.0 @Frequency 1e+9 Hz | ASTM Data | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1e+9 Hz | 0.010 @Frequency 1e+9 Hz | ASTM Data | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | |||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 39.0 μm/m-°C | 21.7 μin/in-°F | ISO 11359 | ||
| CTE, linear, Transverse to Flow | 78.0 μm/m-°C | 43.3 μin/in-°F | ISO 11359 | ||
| Specific Heat Capacity | 2.728 J/g-°C | 0.6520 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft2-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75 | ||
| 200 °C | 392 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||