- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.4
- 缺口沖擊強度: 0.45
- 彎曲強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 4.77
- 硬度: 121.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.1 % | 8.1 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | 0.2 in/min; ASTM Test | ||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ASTM Test | |||
| 50.0 MPa @Temperature 120 °C | 7250 psi @Temperature 248 °F | ISO Data | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ISO Data | |||
| 60.0 MPa @Temperature 80.0 °C | 8700 psi @Temperature 176 °F | ASTM Test | |||
| 150 MPa @Temperature -40.0 °C | 21800 psi @Temperature -40.0 °F | ASTM Test | |||
| 150 MPa @Temperature -40.0 °C | 21800 psi @Temperature -40.0 °F | ISO Data | |||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ASTM Test | |||
| 3.0 % @Temperature -40.0 °C | 3.0 % @Temperature -40.0 °F | ISO Data | |||
| 10 % @Temperature 120 °C | 10 % @Temperature 248 °F | ISO Data | |||
| 10 % @Temperature 120 °C | 10 % @Temperature 248 °F | ASTM Test | |||
| 14 % @Temperature 80.0 °C | 14 % @Temperature 176 °F | ASTM Test | |||
| 14 % @Temperature 80.0 °C | 14 % @Temperature 176 °F | ISO Data | |||
| Tensile Modulus | 6.13 GPa | 889 ksi | 1mm/min; ISO 527 | ||
| 2.02 GPa @Temperature 120 °C | 293 ksi @Temperature 248 °F | ISO Data | |||
| 2.45 GPa @Temperature 80.0 °C | 355 ksi @Temperature 176 °F | ISO Data | |||
| 6.88 GPa @Temperature -40.0 °C | 998 ksi @Temperature -40.0 °F | ISO Data | |||
| Flexural Strength | 160 MPa | 23200 psi | ISO Data | ||
| Flexural Modulus | 4.77 GPa | 692 ksi | ISO Data | ||
| 5.20 GPa | 754 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.450 J/cm @Thickness 3.17 mm | 0.843 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Charpy Impact Unnotched | 3.10 J/cm2 | 14.8 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ISO 75 | ||
| 201 °C | 394 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 275 °C | 527 °F | Injection molding | ||
| Mold Temperature | 95.0 °C | 203 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||