- 熔體流動速率 [g/10min]: 55.0
- 密度 [g/cm3]: 0.923
- 缺口沖擊強度: 29.0
- 拉伸強度 [MPa]: 9.0
- 彎曲強度 [MPa]: 8.3
- 彎曲模量 [MPa]: 0.248
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.923 g/cc | 0.0333 lb/in3 | |
| Viscosity | 21000 cP @Shear Rate 5000 1/s, Temperature 190 °C | 21000 cP @Shear Rate 5000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity |
| 32000 cP @Shear Rate 1000 1/s, Temperature 190 °C | 32000 cP @Shear Rate 1000 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| 40000 cP @Shear Rate 300 1/s, Temperature 190 °C | 40000 cP @Shear Rate 300 1/s, Temperature 374 °F | Apparent Dynamic Viscosity | |
| Melt Flow | 55 g/10 min @Load 2.16 kg | 55 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 8.30 MPa | 1200 psi | |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | |
| Elongation at Break | 160 % | 160 % | |
| Modulus of Elasticity | 0.155 GPa | 22.5 ksi | Molded Sample 2% Secant Modulus |
| Flexural Modulus | 0.248 GPa | 36.0 ksi | |
| Izod Impact, Notched (ISO) | 29.0 kJ/m2 @Temperature -50.0 °C | 13.8 ft-lb/in2 @Temperature -58.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | |