- 熔體流動速率 [g/10min]: 2.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ASTM D1505/D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 230 % | 230 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Elmendorf Tear Strength TD | 90 g | 90 g | gF; ASTM D1922 |
| Dart drop Test | 70.0 g | 0.154 lb | g/F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 8.0 % @Thickness 0.0250 mm | 8.0 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 93 % @Thickness 0.0250 mm | 93 % @Thickness 0.000984 in | 60°; ASTM D2457 |