- 熔體流動(dòng)速率 [g/10min]: 5.0
- 密度 [g/cm3]: 0.936
- 拉伸強(qiáng)度 [MPa]: 21.4
- 彎曲模量 [MPa]: 0.758
- 熱變形溫度 [℃]: 60.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in3 | ASTM D1505 | ||
| ESCR 100% Igepal? | >= 750 hour | >= 750 hour | ASTM D1693 | ||
| Melt Flow | 5.00 g/10 min @Load 2.16 kg, Temperature 190 °C | 5.00 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 11.7 MPa | 1700 psi | 2 in/min; ASTM D638 | ||
| Tensile Strength, Yield | 21.4 MPa | 3100 psi | 2 in/min; ASTM D638 | ||
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 | ||
| Elongation at Yield | 10.0 % | 10.0 % | ASTM D638 | ||
| Flexural Modulus | 0.758 GPa | 110 ksi | 1% Secant; ASTM D790 | ||
| Impact Test | 47.5 J @Temperature 22.2 °C | 35.0 ft-lb @Temperature 72.0 °F | ARM STD test | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| Process | Rotational Molding | ||||
| Region | Europe/Turkey | ||||