- 熔體流動速率 [g/10min]: 58.0
- 密度 [g/cm3]: 1.38
- 吸水率 [%]: 0.4
- 拉伸強度 [MPa]: 100.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 94 cm3/g | 94 cm3/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0041 cm/cm | 0.0041 in/in | ISO 294 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294 | ||
| Melt Flow | 58.0 g/10 min @Load 2.16 kg, Temperature 275 °C | 58.0 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Break | 2.2 % | 2.2 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 6.90 GPa | 1000 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.20 J/cm2 | 20.0 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | |||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 178 °C | 352 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||