- 拉伸強(qiáng)度 [MPa]: 19.7
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 19.7 MPa @Temperature 24.0 °C | 2860 psi @Temperature 75.2 °F | Dry | ||
| 1758 MPa @Temperature -55.0 °C | 255000 psi @Temperature -67.0 °F | Dry | |||
| 1793 MPa @Temperature 71.0 °C | 260100 psi @Temperature 160 °F | Dry | |||
| Tensile Modulus | 131.7 GPa @Temperature 24.0 °C | 19100 ksi @Temperature 75.2 °F | Dry | ||
| 132.4 GPa @Temperature 71.0 °C | 19200 ksi @Temperature 160 °F | Dry | |||
| 140 GPa @Temperature -55.0 °C | 20300 ksi @Temperature -67.0 °F | Dry | |||
| Compressive Yield Strength | 848 MPa @Temperature 71.0 °C | 123000 psi @Temperature 160 °F | Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 1117 MPa @Temperature 24.0 °C | 162000 psi @Temperature 75.2 °F | Dry | |||
| Compressive Modulus | 119.3 GPa @Temperature 71.0 °C | 17300 ksi @Temperature 160 °F | Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 133.1 GPa @Temperature 24.0 °C | 19300 ksi @Temperature 75.2 °F | Dry | |||
| Shear Strength | 38.6 MPa @Temperature 71.0 °C | 5600 psi @Temperature 160 °F | Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) | ||
| 82.0 MPa @Temperature 24.0 °C | 11900 psi @Temperature 75.2 °F | Short Beam, Dry | |||
| Descriptive Properties | |||||
| Dry Resin Content (%) | 37-41 | Prepreg | |||
| Fiber Volume (%) | 0.014 | Laminate | |||
| Flow (%) | 4-16 | ||||
| Wet Resin Content (%) | 52 | Laminate | |||