- 拉伸強度 [MPa]: 13.0
- 彎曲強度 [MPa]: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity Measurement | 2.2 @Temperature 160 °C | 2.2 @Temperature 320 °F | [dNm]; ML, (0.5 RAD); ASTM D5289 | ||
| 3.0 @Temperature 160 °C | 3.0 @Temperature 320 °F | [min]; ts1, (0.5 RAD); ASTM D5289 | |||
| 6.5 @Temperature 160 °C | 6.5 @Temperature 320 °F | [min]; T50, (0.5 RAD); ASTM D5289 | |||
| 12 @Temperature 160 °C | 12 @Temperature 320 °F | [min]; T90, (0.5 RAD); ASTM D5289 | |||
| 17.2 @Temperature 160 °C | 17.2 @Temperature 320 °F | [dNm]; MH, (0.5 RAD); ASTM D5289 | |||
| Mooney Viscosity | 50 @Temperature 100 °C | 50 @Temperature 212 °F | [MU]; ML 1+4, massed sample; ASTM D1646-99 (7.2.2) | ||
| Ash | 0.10 % | 0.10 % | ASTM D5667 | ||
| Collected Volatile Condensable Material | 0.20 % | 0.20 % | ASTM D5668 | ||
| Storage Temperature | <= 30.0 °C | <= 86.0 °F | |||
| Chemical Properties | Metric | English | Comments | ||
| Acid Value | 4.9 | 4.9 | % Organic Acid; ASTM D5775 | ||
| Styrene Content | 23.5 % | 23.5 % | Bound Styrene; ASTM D5775 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 23.0 MPa | 3340 psi | Die C (35 min / 145°C); ASTM D412 | ||
| Tensile Strength, Yield | 13.0 MPa @Strain 300 % | 1890 psi @Strain 300 % | ASTM D412 | ||
| Elongation at Break | 460 % | 460 % | ASTM D412 | ||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | >= 12.0 Month | >= 12.0 Month | |||
| Descriptive Properties | |||||
| Accelerator (TBBS) wt% | 1 | ASTM 3185-1A | |||
| Carbon Black wt% | 50 | ASTM 3185-1A; IRB 7 | |||
| Stearic Acid wt% | 1 | ASTM 3185-1A | |||
| Sulfur content, % | 1.75 | ASTM 3185-1A | |||
| Total Extractables % | 32.5 | ASTM D5774 | |||
| Zinc Oxide wt% | 3 | ASTM 3185-1A | |||