- 彎曲強度 [MPa]: 15.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | |||
| Brookfield Viscosity | 3000 cP | 3000 cP | |||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 73 - 77 | 73 - 77 | ASTM D2240 | ||
| Tensile Strength, Ultimate | 15.9 MPa | 2300 psi | ASTM D412 | ||
| Elongation at Break | 650 % | 650 % | ASTM D412 | ||
| Tear Strength | 33.3 kN/m | 190 pli | ASTM 4-624-54 D Die C | ||
| Processing Properties | Metric | English | Comments | ||
| Moisture Content | 2.8 % | 2.8 % | 2 weeks; ASTM D570 | ||
| Cure Time | 480 - 840 min @Temperature 24.0 °C | 8.00 - 14.0 hour @Temperature 75.2 °F | demold time | ||
| 4320 - 7200 min @Temperature 24.0 °C | 72.0 - 120 hour @Temperature 75.2 °F | full cure | |||
| Pot Life | 25 min @Temperature 25.0 °C | 25 min @Temperature 77.0 °F | work life | ||
| 40 min @Temperature 24.0 °C | 40 min @Temperature 75.2 °F | gel time (180g) | |||
| Descriptive Properties | |||||
| Mix Ratio | 100:45 by weight (resin/hardener) | ||||