- 拉伸強度 [MPa]: 75.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.30 - 1.40 g/cc @Thickness 1.57 mm | 1.30 - 1.40 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 3.2 % @Thickness 1.57 mm | 3.2 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90 - 110 @Thickness 1.57 mm | 90 - 110 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 75.2 MPa @Thickness 1.57 mm | 10900 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 87.6 MPa @Thickness 1.57 mm | 12700 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 8.96 GPa @Thickness 1.57 mm | 1300 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 11.7 GPa @Thickness 1.57 mm | 1700 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 143 MPa @Thickness 1.57 mm | 20700 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 159 MPa @Thickness 1.57 mm | 23000 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 241 MPa @Thickness 12.7 mm | 35000 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 96.5 MPa @Thickness 15.7 mm | 14000 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 0.908 J/cm @Thickness 12.7 mm | 1.70 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 1.01 J/cm @Thickness 12.7 mm | 1.90 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 11.8 kV/mm @Thickness 1.57 mm | 300 kV/in @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S.T. | ||
| 21.7 kV/mm @Thickness 1.57 mm | 550 kV/in @Thickness 0.0620 in | Cond A; ASTM D229 S.T. | |||
| Dielectric Breakdown | 40000 V @Thickness 1.57 mm | 40000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 20.0 μm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 11.1 μin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 22.0 μm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 12.2 μin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1900 lb | 0.5", ASTM D229 | |||
| Color | Natural | ||||