- 密度 [g/cm3]: 0.0288
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0288 g/cc | 0.00104 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.586 MPa | >= 85.0 psi | Bare, min |
| >= 0.655 MPa | >= 95.0 psi | Stabilized, min | |
| 0.758 MPa | 110 psi | Bare, typ | |
| 0.827 MPa | 120 psi | Stabilized, typ | |
| Compressive Modulus | 0.0483 GPa | 7.00 ksi | Stabilized, typ |
| Shear Modulus | 0.0138 GPa | 2.00 ksi | Plate Shear, L Direction, typ |
| 0.0207 GPa | 3.00 ksi | Plate Shear, W Direction, typ | |
| Shear Strength | >= 0.310 MPa | >= 45.0 psi | Plate Shear, L Direction, min |
| >= 0.345 MPa | >= 50.0 psi | Plate Shear, W Direction, min | |
| 0.448 MPa | 65.0 psi | Plate Shear, L Direction, typ | |
| 0.483 MPa | 70.0 psi | Plate Shear, W Direction, typ | |