- 密度 [g/cm3]: 0.032
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0320 g/cc | 0.00116 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.689 MPa | >= 100 psi | Bare, min |
| >= 0.724 MPa | >= 105 psi | Stabilized, min | |
| 0.827 MPa | 120 psi | Bare, typ | |
| 0.965 MPa | 140 psi | Stabilized, typ | |
| Compressive Modulus | 0.0758 GPa | 11.0 ksi | Stabilized, typ |
| Shear Modulus | 0.0145 GPa | 2.10 ksi | Plate Shear, W Direction, typ |
| 0.0296 GPa | 4.30 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.310 MPa | >= 45.0 psi | Plate Shear, W Direction, min |
| 0.414 MPa | 60.0 psi | Plate Shear, W Direction, typ | |
| >= 0.621 MPa | >= 90.0 psi | Plate Shear, L Direction, min | |
| 0.758 MPa | 110 psi | Plate Shear, L Direction, typ | |