- 熔體流動(dòng)速率 [g/10min]: 34.2
- 密度 [g/cm3]: 1.32
- 缺口沖擊強(qiáng)度: 9.6
- 斷裂伸長(zhǎng)率 [%]: 67.0
- 彎曲強(qiáng)度 [MPa]: 44.8
- 彎曲模量 [MPa]: 2.245
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm | 0.0010 - 0.0020 in/in | |
| Melt Flow | 34.2 g/10 min | 34.2 g/10 min | Condition F; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | ASTM D638 |
| Flexural Yield Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 2.245 GPa | 325.6 ksi | ASTM D790 |
| Izod Impact, Notched | 9.60 J/cm @Thickness 3.17 mm | 18.0 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | annealed; ASTM D648 |
| Flammability, UL94 | 5VA | 5VA | V-0, UL Standard 94 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 157 - 196 °C | 315 - 385 °F | |
| Melt Temperature | 196 - 207 °C | 385 - 405 °F | |
| Mold Temperature | 32.2 - 60.0 °C | 90.0 - 140 °F | |
| Drying Temperature | 54.4 °C | 130 °F | |
| Dry Time | 4 hour | 4 hour | Usually not needed |