| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | |||
| 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | |||
| Water Absorption | 0.78 % @Thickness 2.00 mm |
0.78 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Moisture Absorption | 0.230 % @Thickness 2.00 mm |
0.230 % @Thickness 0.0787 in |
Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | ISO 527-1/-2 | ||
Tensile Stress  |
16.22 MPa @Strain 0.260 %, Temperature 40.0 °C |
2353 psi @Strain 0.260 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
| 17.6 MPa @Strain 0.400 %, Temperature 90.0 °C |
2550 psi @Strain 0.400 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 43.3 MPa @Strain 0.580 %, Temperature 23.0 °C |
6280 psi @Strain 0.580 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 46.1 MPa @Strain 1.62 %, Temperature 90.0 °C |
6690 psi @Strain 1.62 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 53.1 MPa @Strain 2.80 %, Temperature 90.0 °C |
7700 psi @Strain 2.80 %, Temperature 194 °F |
ISO 11403-1 -2 | |||
| 55.58 MPa @Strain 0.980 %, Temperature 40.0 °C |
8061 psi @Strain 0.980 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 76.95 MPa @Strain 1.14 %, Temperature 23.0 °C |
11160 psi @Strain 1.14 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 78.69 MPa @Strain 1.71 %, Temperature 40.0 °C |
11410 psi @Strain 1.71 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 97.03 MPa @Strain 1.71 %, Temperature 23.0 °C |
14070 psi @Strain 1.71 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 155 MPa | 22500 psi | ISO 178 | ||
| Secant Modulus | 4.29 GPa @Strain 1.93 %, Temperature 40.0 °C |
622 ksi @Strain 1.93 %, Temperature 104 °F |
ISO 11403-1 -2 | ||
| 5.30 GPa @Strain 1.91 %, Temperature 23.0 °C |
769 ksi @Strain 1.91 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 5.67 GPa @Strain 0.980 %, Temperature 40.0 °C |
823 ksi @Strain 0.980 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 6.24 GPa @Strain 0.260 %, Temperature 40.0 °C |
905 ksi @Strain 0.260 %, Temperature 104 °F |
ISO 11403-1 -2 | |||
| 6.75 GPa @Strain 1.14 %, Temperature 23.0 °C |
979 ksi @Strain 1.14 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| 7.47 GPa @Strain 0.580 %, Temperature 23.0 °C |
1080 ksi @Strain 0.580 %, Temperature 73.4 °F |
ISO 11403-1 -2 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180/1A | ||
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | ISO 180/1U | ||
| 33.0 kJ/m² @Temperature -30.0 °C |
15.7 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U | |||
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA | ||
| 0.650 J/cm² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 7500 MPa @Time 3600 sec |
1.09e+6 psi @Time 1.00 hour |
ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 6000 MPa @Time 3.60e+6 sec |
870000 psi @Time 1000 hour |
ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
IEC 60250 | ||
| 3.7 @Frequency 100 Hz |
3.7 @Frequency 100 Hz |
IEC 60250 | |||
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 60243-1 | ||
| 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
Short Time; IEC 60243-1 | |||
| 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
20s; IEC 60243-1 | |||
| 29.0 kV/mm @Thickness 1.00 mm |
737 kV/in @Thickness 0.0394 in |
Short Time; IEC 60243-1 | |||
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
ASTM D150 | ||
| 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
IEC 60250 | |||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
IEC 60250 | |||
| 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
ASTM D150 | |||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.90 J/g-°C | 0.454 BTU/lb-°F | |||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | of melt | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 | ||
| Oxygen Index | 27 % | 27 % | ISO 4589-1/-2 | ||
| De |
|||||
| Additives | Release agent | ||||
| Delivery form | Pellets | ||||
| Part Marking Code | >PBT+ASA-GF20FR(17)< | ISO 11469 | |||
| Processing | Injection Moulding | ||||
| Regional Availability | Asia Pacific | ||||
| Europe | |||||
| Global | |||||
| Near East/Africa | |||||
| North America | |||||
| South and Central America | |||||
| Resin Identification | PBT+ASA-GF20FR(17) | ||||
| UL recognition | UL | ||||
圖：
上海松翰塑化科技有限公司！本公司承諾，假一賠百！所有產(chǎn)品都是原廠家，原包裝一線獨(dú)家營(yíng)銷！
我司所銷售所有產(chǎn)品均為原廠原包，均可提供相關(guān)資料報(bào)告（如：物性表，MSDS報(bào)告，UL報(bào)告，COA報(bào)告，SGS報(bào)告，F(xiàn)DA等）！
歡迎新老客戶來電或QQ咨詢：
聯(lián)系人：李先生
聯(lián)系電話；13636696005
聯(lián)系QQ；1020580970
聯(lián)系郵箱；1020580970@qq.com